Influence of Triangle Structure Defect on the Carrier Lifetime of the 4H-SiC Ultra-Thick Epilayer

Effect of triangle structure defects in a 180-μm-thick as-grown n-type 4H-SiC homoepitaxial layer on the carrier lifetime is quantitatively analyzed, which is grown by a horizontal hot-wall chemical vapor deposition reactor. By microwave photoconductivity decay lifetime measurements and photoluminescence measurements, the results show that the average carrier lifetime of as-grown epilayer across the whole wafer is 2.59 μs, while it is no more than 1.34 μs near a triangle defect (TD). The scanning transmission electron microscope results show that the triangle structure defects have originated from 3C-SiC polytype and various types of as-grown stacking faults. Compared with the as-grown stacking faults, the 3C-SiC polytype has a great impact on the lifetime. The reduction of TD is essential to increasing the carrier lifetime of the as-grown thick epilayer.

Source:IOPscience

For more information, please visit our website: www.semiconductorwafers.net,

send us email at angel.ye@powerwaywafer.com or powerwaymaterial@gmail.com